Amphiphilic triblock copolymers with PEGylated hydrocarbon structures as environmentally friendly marine antifouling and fouling-release coatings Zhaoli Zhou David R. Calabrese Warren Taylor John A. Finlay Maureen E. Callow James A. Callow Daniel Fischer Edward J. Kramer Christopher K. Ober 10.6084/m9.figshare.997711.v3 https://tandf.figshare.com/articles/journal_contribution/Amphiphilic_triblock_copolymers_with_PEGylated_hydrocarbon_structures_as_environmentally_friendly_marine_antifouling_and_fouling_release_coatings/997711 <div><p>The ideal marine antifouling (AF)/fouling-release (FR) coating should be non-toxic, while effectively either resisting the attachment of marine organisms (AF) or significantly reducing their strength of attachment (FR). Many recent studies have shown that amphiphilic polymeric materials provide a promising solution to producing such coatings due to their surface dual functionality. In this work, poly(ethylene glycol) (PEG) of different molecular weights (M<sub>w</sub> = 350, 550) was coupled to a saturated difunctional alkyl alcohol to generate amphiphilic surfactants (PEG-hydrocarbon-OH). The resulting macromolecules were then used as side chains to covalently modify a pre-synthesized PS<sub>8</sub> <sub>K</sub>-<i>b</i>-P(E/B)<sub>25</sub> <sub>K</sub>-<i>b</i>-PI<sub>10</sub> <sub>K</sub> (SEBI or K3) triblock copolymer, and the final polymers were applied to glass substrata through an established multilayer surface coating technique to prepare fouling resistant coatings. The coated surfaces were characterized with AFM, XPS and NEXAFS, and evaluated in laboratory assays with two important fouling algae, <i>Ulva linza</i> (a green macroalga) and <i>Navicula incerta</i>, a biofilm-forming diatom. The results suggest that these polymer-coated surfaces undergo surface reconstruction upon changing the contact medium (polymer/air <i>vs</i> polymer/water), due to the preferential interfacial aggregation of the PEG segment on the surface in water. The amphiphilic polymer-coated surfaces showed promising results as both AF and FR coatings. The sample with longer PEG chain lengths (M<sub>w</sub> = 550 g mol<sup>−1</sup>) exhibited excellent properties against both algae, highlighting the importance of the chemical structures on ultimate biological performance. Besides reporting synthesis and characterization of this new type of amphiphilic surface material, this work also provides insight into the nature of PEG/hydrocarbon amphiphilic coatings, and this understanding may help in the design of future generations of fluorine-free, environmentally friendly AF/FR polymeric coatings.</p></div> 2014-06-03 15:23:12 amphiphilic triblock copolymers pegylated hydrocarbon structures environmentally antifouling fouling-release coatings