Basic properties mapping of anodic oxides in the hafnium–niobium–tantalum ternary system

Download (1.19 MB)
Version 2 2018-08-13, 09:54
Version 1 2018-07-13, 09:02
figure
posted on 2018-08-13, 09:54 authored by Andrei Ionut Mardare, Cezarina Cela Mardare, Jan Philipp Kollender, Silvia Huber, Achim Walter Hassel

A thin film combinatorial library deposited by co-sputtering of Hf, Nb and Ta was employed to characterise fundamental properties of the Hf-Nb-Ta system. Compositional mappings of microstructure and crystallography revealed similarities in alloy evolution. Distinct lattice distortion was observed upon addition of hexagonal Hf, leading to amorphisation of alloys containing more than 32 at.% Hf and less than 27 and 41 at.% Nb and Ta, respectively. Volta potential and open circuit potential mappings indicated minimal values for the highest Hf concentration. Localised anodisation of the library by scanning droplet cell microscopy revealed valve metal behaviour. Oxide formation factors above 2 nm V−1 were identified in compositional zones with high amounts of Nb and Ta. Fitting of electrochemical impedance spectroscopy data allowed electrical permittivity and resistivity of mixed oxides to be mapped. Their compositional behaviours were attributed to characteristics of the parent metal alloys and particularities of the pure oxides. Mott–Schottky analysis suggested n-type semiconductor properties for all Hf–Nb–Ta oxides studied. Donor density and flat-band potential were mapped compositionally, and their variations were found to be related mainly to the Nb amount. Synergetic effects were identified in mappings of Hf-Nb-Ta parent metals and their anodic oxides.

Funding

This work was supported by the Christian Doppler Forschungsgesellschaft [COMBOX]; Österreichische Forschungsförderungsgesellschaft mbH [CEST-UPPER].

History